Modell nr: A588 GR.A/ GR.B
Standard-: AiSi, ASTM, bs, DÅN, GB, JIS
Härstamning: Kina
Arter: Stålplåt
Produktionsprocess: Varmvalsad
Ansökan: Kokplatta, Behållarplatta, Fartygsplatta
Speciellt Stål: Slitstarkt stål, Höghållfast stålplåt
Tolerans: ± 1%
Kategori: Platta med låg legering, Ship Steel Plate, Pannfartygsplatta, Varmvalsat stålplåt
Bearbetningstjänst: Böjning, Svetsning, Avkokning, Skärande, Stansning
Förpackning: Standard marinförpackning, eller som krävs av kunden
Produktivitet: 10000 Tons Per Month
Transportfordon: Ocean,Land,Express
Stödja: 10000 Tons Per Month
Certifikat: ISO 9001
Hamn: Qingdao,Tianjin,Shanghai
Betalning Typ: L/C,T/T,D/P
Incoterm: FOB,CFR,CIF,EXW
Lagerområde:
Standard: ASTM A588 klass A, klass B, klass K
Tjockleksområde: 5 - 150 mm
Breddsintervall: 900 - 4800 mm
Längdintervall: 3000 - 12000 mm
Stålskärningstjänster: Låga skärning av stål, laserskuret stål, skärande stålplåt
ASTM A588 Grad A, B är specifikationen för atmosfärisk korrosionsstruktur av högstyrka låglegering, avkastningsstyrka minimum 50 KSI 345 MPa. Det täcker klass A, klass B och klass K, material inkluderar stålformer, plattor och staplar för svetsade, nitade eller bultade konstruktion men är främst avsedd för användning i svetsade broar och byggnader där besparingar i vikt eller tillagd hållbarhet är viktiga.
De huvudsakliga atmosfäriska korrosionsbeständiga stålkvaliteterna är: Corten A, Corten B; ASTM A588; ASTM A242; EN10025-5 EN10155 S235J0W, S235J2W, S355J0WP, S355J2WP, S355J0W; TBT1979 09CUPCRNI-A, 05CUPCRNI, GBT4171 Q355GNH, Q235NH, Q295NH, Q355NH; Jis G3125 Spa-H, Spa-C; och så vidare .
ASTM -standarder:
A6/A6M -specifikation för allmänna krav för rullade stålstålstänger, plattor, former och arkstap
G101 Guide för att uppskatta atmosfärisk korrosionsmotstånd för låglegeringstål
Strukturprodukter som tillhandahålls enligt denna specifikation ska överensstämma med kraven i den aktuella upplagan av specifikationen A6/A6M, för den specifika strukturella produkten som beställs, såvida inte en konflikt finns, i vilket fall denna specifikation ska råda.
Spolar är uteslutna från kvalifikation till denna specifikation tills de bearbetas till en färdig strukturell produkt. Det betyder att produkterna har skurits till individuella längder från en spole.
Stålet ska göras till finkorn.
ASTM A588 GRADE A, ASTM A588 GRADE B, ASTM A588 GRADE K.
|
A588/A588M TABLE1 Chemical Requirements (Heat Analysis) |
|||
|
|
Composition,% |
||
|
Element |
Grade A |
Grade B |
Grade K |
|
Carbon ① |
0.19 max |
0.20 max |
0.17 max |
|
Manganese ① |
0.80-1.25 |
0.75-1.35 |
0.50-1.20 |
|
Phosphorus ③ |
0.030 max |
0.030 max |
0.030 max |
|
Sulfur ③ |
0.030 max |
0.030 max |
0.030 max |
|
Silicon |
0.30-0.65 |
0.15-0.50 |
0.25-0.50 |
|
Nickel |
0.40 max |
0.50 max |
0.40 max |
|
Chromium |
0.40-0.65 |
0.40-0.70 |
0.40-0.70 |
|
Molybdenum |
|
|
0.10 max |
|
Copper |
0.25-0.40 |
0.20-0.40 |
0.30-0.50 |
|
Vanadium |
0.02-0.10 |
0.01-0.10 |
|
|
Columbium |
|
|
0.005-0.05 ② |
|
① For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50%. ② For plates under in.[13 mm] in thickness, the minimum columbium is waived. ③ A maximum phosphorus content of 0.04% and a maximum sulfur content of 0.05% are permitted for the following materials. .Structural shapes .Bars .Plates with widths up to and including 15 in. [380 mm] |
|||
|
A588/A588M TABLE2 Tensile Requirements ① |
||||
|
NoTE I-Where"..."appears in this table, there is no requirement |
||||
|
|
|
Plates and Bars |
|
Structural Shapes |
|
For Thicknesses |
For Thicknesses |
For Thicknesses |
All |
|
|
4 in.[100mm] and Under |
Over 4 in.[100mm] to 5 in.[125mm] incl |
Over 5 in.[125mm] to 8 in.[200mm] incl |
||
|
Tensile strength,min,ksi [MPa] |
70[485] |
67[460] |
63[435] |
70[485] |
|
Yield point,min,ksi [MPa] |
50[345] |
46[315] |
42[290] |
50[345] |
|
Elongation in 8in.[200 mm].min.% |
18 ②③ |
... |
... |
18 ③ |
|
Elongation in 2 in.[50 mm].min,% |
21 ②③ |
21 ②③ |
21 ②③ |
21 ④ |
|
① See specimen orientation under the Tension Tests section of Specification A6/A6M. ② Elongation not required to be determined for floor plate. ③ For plates wider than 24 in. [600mm], the elongation requirement is reduced two percentage points. See elongation requirement adjustments in the Tension Tests section of Specification A6/A6M. ④ For wide flange shapes with flange thickness over 3 in. (75mm), elongation in 2in.[50mm] of 18% minimum applies. |
||||
Tilläggskrav ska inte tillämpas såvida de inte anges i beställningen eller kontraktet. Standardiserade tilläggskrav för användning vid köparen listas i specifikationen A6/A6M. De som anses vara lämpliga för användning med denna specifikation listas:
S2. Produktanalys
S3. Simulerad värmebehandling efter svetsen av mekaniska testkuponger.
S5. Charpy V-Norch Impact Test
S6. Drop-weight-test för material 0,625 i 16 mm och över i tjocklek.
S8. Ultraljudsundersökning.
S15. Reducion av mätning av arean.
S18. Maximal draghållfasthet
S30. Charpy V-Notch Impact Test för strukturella former alternativa kärnplats och
S32. Enskilda buntar
A242 -plattan är låglegeringsstål med viktbesparingar och atmosfärisk korrosionsbeständighet.
Från kemisk sammansättning ASTM A242 har lägre kol, fosfor och svavelkontet, den har bara en typ, och A588 har tre typer, A588 klass A, B, K.
ASTM A588 Grad A -plattan motsvarar Corten en stålplatta. ASTM A242 -plattan motsvarar Corten B. Jämfört med vanligt låglegering med hög hållfasthet, såsom A572 Grad 50, har ASTM A588 och ASTM A242 fördelar med väderbeständiga prestationer.
Med ett ord ASTM A588 täcker fler intervall av väderstål än A242.
Vårt leveransområde
Standard: ASTM A588 klass A, klass B, klass K
Tjockleksområde: 5 - 150 mm
Breddsintervall: 900 - 4800 mm
Längdintervall: 3000 - 12000 mm
Stålskärningstjänster: Flamskärning av stål, laserskuren stål, vattenjetskärning av stålplåt, plasmaskärning.